TR-P995 Unsaturated polyester resins
TR-P995 Unsaturated polyester resins
Features and main purposes:
TR－P995 is a kind of unsaturated polyester resin synthesized with main raw materials of isophthalic acid, maleic anhydride and standard diatomic alcohol, having dissolved in styrene.Medium viscosity and high reactivity，pultrusion products made with it have high strength, good toughness and heat resistance.Suitable for pultrusion process, suitable for making tent poles, fishing rods and other products.
Specification of liquid resin：(25℃)：
|
Items |
Unit |
Testing result |
Test Method |
|
Appearance |
--- |
Transparent yellowish liquid |
GB/T8237.6.1.1 |
|
Viscosity |
Pa·s |
0.6-0.8 |
GB/T 7193-2008 |
|
Acid Value |
mgKOH/g |
16-22 |
GB/T 2895-2008 |
|
Geltime |
Min（25℃） |
6.0-10.0 |
GB/T 7193-2008 |
|
Shelf life |
H（80℃） |
≥24 |
GB/T 7193-2008 |
Note:25°C water bath, adding 2ml peroxide methyl ethyl ketone solution and 4ml iso-octanoic acid cobalt solution into 100g resin
Specification of casting resin(typical value):
| Items |
Unit |
Test performance |
Test Method |
|
Casting matrix |
|||
|
Tensile strength |
MPa |
≥60 |
GB/T2567-2008 |
|
Tensile Modulus |
MPa |
≥3000 |
GB/T2567-2008 |
|
Break elongation rate |
% |
≥3 |
GB/T2567-2008 |
|
Flexible strength |
MPa |
≥100 |
GB/T2567-2008 |
|
Flexible Modulus |
MPa |
≥3000 |
GB/T2567-2008 |
|
Heat Distortion Temp |
℃ |
≥75 |
GB/T1634-2004 |
|
Barcol hardness |
--- |
≥45 |
GB/T3854-2005 |
Note: (1) Casting matrix sample is made according to GB/T8237-2005; with temperature of 25°C, curing system: promoter RCA 1.0%, Curing agent M-50 1.5%.
(2) Post-curing treatment of casting matrix: room temperature×24 Hours+60°C×3 Hours+80°C×2 Hours;