TR-968 Unsaturated polyester resins
TR-968 Unsaturated polyester resins
Features and main purposes:
TR－608 is a kind of unsaturated polyester resin synthesized with main materials of phthalic anhydride and standard diatomic alcohol, having dissolved in styrene，Promoters have been added.It features medium viscosity and moderate reactivity. With excellent mechanical properties.Applicable for injection molding crafts, especially for imitation granite/marble and handicrafts, with features of excellent strength, toughness, water-resistance and weathering-resistance.
Specification of liquid resin：(25℃)：
| Items |
Unit |
Testing result |
Test Method |
|
Appearance |
--- |
pre-promoting thixotropic liquid |
GB/T8237.6.1.1 |
|
Viscosity |
Pa·s |
0.4-0.77 |
GB/T 7193-2008 |
|
Acid Value |
mgKOH/g |
15-27 |
GB/T 2895-2008 |
|
Geltime |
Min（25℃） |
9-16 |
GB/T 7193-2008 |
|
Shelf life |
H（80℃） |
≥24 |
GB/T 7193-2008 |
Note：25°C water bath, adding 2ml methyl ethyl ketone peroxide solution into the 100g resins.
Casting matrix(typical valu)：
| Items |
Unit |
Test performance |
Test Method |
|
Casting matrix |
|||
|
Tensile strength |
MPa |
≥60 |
GB/T2567-2008 |
|
Tensile Modulus |
MPa |
≥2500 |
GB/T2567-2008 |
|
Break elongation rate |
% |
≥3.0 |
GB/T2567-2008 |
|
Flexible strength |
MPa |
≥90 |
GB/T2567-2008 |
|
Flexible Modulus |
MPa |
≥3000 |
GB/T2567-2008 |
|
Heat Distortion Temp |
℃ |
60±5 |
GB/T1634-2004 |
|
Barcol hardness |
--- |
≥45 |
GB/T3854-2005 |
Note: (1) Casting matrix sample is made according to GB/T8237-2005; with temperature of 25°C, curing system: promoter RCA 1.0%, Curing agent M-50 1.5%.
(2) Post-curing treatment of casting matrix: room temperature×24 Hours+60°C×3 Hours+80°C×2 Hours;