一、特点及主要用途：
TR N3250PT is ortho-type unsaturated polyester resin with medium viscosity and medium reactivity for general purpose use,with medium gel and fast cure characteristics,good fiber wet out,especially intended for the FRP parts production requiring high productivity, It is promoted,thixotropied but non-waxed
二、液体树脂技术指标：
| 项目 |
单位 |
测试指标 |
测试方法 |
|
外观 |
--- |
粉色触变液体 |
GB/T8237.6.1.1 |
|
粘度 |
CPa·s |
350-450 |
GB/T 7193-2008 |
|
酸值 |
mgKOH/g |
14-25 |
GB/T 2895-2008 |
|
凝胶时间 |
Min（30℃） |
15-20 |
GB/T 7193-2008 |
|
稳定性 |
月（25℃） |
3-4 |
GB/T 7193-2008 |
|
触变指数 |
|
2.0-2.2 |
|
注：30℃水浴，100g树脂中加1g 固化剂M-50.
三、浇铸体物理性能(仅供参考)：
| 项目 |
单位 |
测试性能 |
测试方法 |
|
浇铸体 |
|||
|
拉伸强度 |
MPa |
≥65 |
GB/T2567-2008 |
|
拉伸弹性模量 |
MPa |
≥3000 |
GB/T2567-2008 |
|
断裂伸长率 |
% |
≥3 |
GB/T2567-2008 |
|
弯曲强度 |
MPa |
≥100 |
GB/T2567-2008 |
|
弯曲弹性模量 |
MPa |
≥3000 |
GB/T2567-2008 |
|
热变形温度 |
℃ |
≥55 |
GB/T1634-2004 |
|
巴柯尔硬度 |
--- |
≥40 |
GB/T3854-2005 |
注：(1)浇铸体制样方法按GB/T8237-2005执行；温度25℃，固化系统：固化剂M-50 1%。
(2)浇铸体后固化处理：室温×24小时＋60℃×3小时+80℃×2小时；
四．注意事项：
1、使用前请在包装桶中搅拌均匀，或将包装桶中的树脂全部倒出后搅拌均匀，再使用。
2、运输时应符合国务院《化学危险品安全管理条例》第五章化学危险物品的运输装卸规定。产品应贮存在25℃以下阴凉处，避免火种，隔离热源，25℃以下贮存保质期为3个月。