TR-196 Unsaturated polyester resins
TR-196 Unsaturated polyester resins
Features and main purposes:
TR－196 is a kind of unsaturated polyester resin synthesized with main materials of phthalic anhydride and standard diatomic alcohol, having dissolved in styrene,with medium viscosity and reactivity, after curing, it shows high mechanical properties. can be widely used in a variety of FRP products and molding process like hand layup and winding.
Specification of liquid resin：(25℃)：：
| Items |
Unit |
Testing result |
Test Method |
|
Appearance |
--- |
Transparent yellowish viscous liquid |
GB/T8237.6.1.1 |
|
Viscosity |
Pa·s |
0.63-1.20 |
GB/T 7193-2008 |
|
Acid Value |
mgKOH/g |
17-24 |
GB/T 2895-2008 |
|
Geltime |
Min（25℃） |
9.1-16.9 |
GB/T 7193-2008 |
|
Shelf life |
H（80℃） |
≥24 |
GB/T 7193-2008 |
Note: 25°C gel time test: 25°C water bath, adding 1ml peroxide methyl ethyl ketone solution and 2ml iso-octanoic acid cobalt solution into 50g resin
Casting matrix(typical valu)：
| Items |
Unit |
Test performance |
Test Method |
|
Casting matrix |
|||
|
Tensile strength |
MPa |
≥60 |
GB/T2567-2008 |
|
Tensile Modulus |
MPa |
≥3000 |
GB/T2567-2008 |
|
Break elongation rate |
% |
≥3.0 |
GB/T2567-2008 |
|
Flexible strength |
MPa |
≥100 |
GB/T2567-2008 |
|
Flexible Modulus |
MPa |
≥3500 |
GB/T2567-2008 |
|
Heat Distortion Temp |
℃ |
≥60 |
GB/T1634-2004 |
|
Barcol hardness |
--- |
≥40 |
GB/T3854-2005 |
Note: (1) Casting matrix sample is made according to GB/T8237-2005; with temperature of 25°C, curing system: promoter RCA 1.0%, Curing agent M-50 1.5%.
(2) Post-curing treatment of casting matrix: room temperature×24 Hours+60°C×3 Hours+80°C×2 Hours;